A method for manufacturing a dental mill blank, said method being characterized by comprising contacting a molded article formed of an inorganic filler, which is obtained by press-molding the inorganic filler, with a polymerizable monomer-containing composition and then polymerizing and curing the polymerizable monomer. According to the manufacturing method of the present invention, a dental mill blank that has a high inorganic powder content and an excellent mechanical strength can be obtained. The dental mill blank thus obtained is preferably usable in producing a dental prosthesis having a high mechanical strength and an excellent lubricant durability, by cutting with the use of, for example, a CAD/CAM system.L'invention concerne un procédé pour la fabrication d'un ciment dentaire blanc broyé, ledit procédé étant caractérisé en ce qu'il comprend la mise en contact d'un article moulé formé d'une charge inorganique, qui est obtenu par moulage à la presse de la charge inorganique, avec une composition contenant un monomère polymérisable et ensuite la polymérisation et le durcissement du monomère polymérisable. Selon le procédé de fabrication de la présente invention, un ciment dentaire blanc broyé qui a une teneur élevée en poudre inorganique et une excellente résistance mécanique peut être obtenu. Le ciment dentaire blanc broyé ainsi obtenu est de préférence utilisable dans la production d'une prothèse dentaire ayant une résistance mécanique élevée et une excellente durabilité de lubrifiant, par découpage avec l'utilisation, par exemple, d'un système CAD/CAM.無機充填材をプレス成形してなる無機充填材成形体と重合性単量体含有組成物を接触させて、該重合性単量体を重合硬化させることを特徴とする、歯科用ミルブランクの製造方法。本発明の製造方法を用いると、無機粉末含有量が高く、機械的強度に優れる歯科用ミルブランクが得られる。また得られる歯科用ミルブランクは、例えば、ＣＡＤ／ＣＡＭシステムを用いて切削加工することによって、高い機械的強度と優れた滑沢耐久性を有する歯科補綴物を作製するために、好適に用いられる。