A medical porous metal material for dental bone replacement and preparation method therefor, produced as follows: mixing tantalum powder, polyvinyl alcohol, and sodium bicarbonate into a powder mixture, press-forming the powder mixture into an organic foamed body under 50 to 100 Mpa, then degreasing, sintering, cooling, and performing a heating process. The heating process step comprises: within a vacuum degree of 10-4 to 10-3 Pa, increasing the temperature to 800 to 900°C at a speed of 10 to 20°C/min, maintaining the temperature for 240 to 480 minutes, cooling to 400°C at a speed of 2 to 5°C/min, maintaining the temperature for 120 to 300 minutes, and cooling together with the furnace to room temperature. The medical porous tantalum material produced has a diameter of 10 to 25 μm, a porosity of 25% to 35%, an elastic modulus of 6.0 to 7.0 Gpa, and an elongation rate of 14% to 15%.Matériau métallique poreux de substitution de los dentaire à usage médical et son procédé de préparation. Ce matériau est formé de poudre de tantale et dun mélange de poudre synthétique dalcool polyvinylique et de bicarbonate de sodium. Entre 50 et 100 MPa, la poudre synthétique est comprimée jusquà obtention, dans un corps mousseux organique, dun moulage, décrassage, frittage, refroidissement et traitement thermique, lequel traitement thermique présente un degré de vide de 10-4 Pa et 10-3 Pa, avec un chauffage de 10 à 20°C/min atteignant entre 800 et 900°C pour préserver la chaleur pendant 240 à 480 min, puis un refroidissement de 2 à 5°C/min pour atteindre jusquà 400°C afin de préserver la chaleur pendant 120 à 300 min, après quoi le four est refroidi à température ambiante. Le diamètre des pores du matériau de tantale poreux à usage médical est de 10 à 25 μm, le pourcentage de porosité va de 25 à 35 %, le module délasticité va de 6,0 à 7,0 GPa et lallongement atteint entre 14 et 15 %.