PROBLEM TO BE SOLVED: To provide a medical tool comprising a cover layer (lubrication layer) exerting excellent durability.SOLUTION: There is provided a method of producing a medical tool comprising a substrate layer and a lubrication layer carried on at least a part of the substrate layer. By reacting a polyperoxide comprising a peroxide group with a reactive monomer comprising an epoxy group at a temperature more than 65°C to less than 85°C for more than 15 minutes to less than 120 minutes, a reactive polymer having 30,000 to 80,000 of weight average molecular weight (Mw) and 10 to 30 J/g of crystal melting enthalpy (ΔH) and comprising an epoxy group and a peroxide group is obtained. Reacting the reactive polymer with at least one hydrophilic monomer selected from a group consisting of acrylamide and acrylamide derivatives to produce a block copolymer. Furthermore, by applying the block copolymer onto the substrate layer, the lubrication layer is formed on the substrate.SELECTED DRAWING: NoneCOPYRIGHT: (C)2016,JPO&INPIT【課題】 優れた耐久性を発揮する被覆層(潤滑層)を有する医療用具を提供する。【解決手段】 基材層と、前記基材層の少なくとも一部に担持された潤滑層と、を備える医療用具の製造方法であって、パーオキサイド基を有するポリ過酸化物を、エポキシ基を有する反応性単量体と、65℃を超えて85℃未満の温度で15分を超えて120分未満の間、反応させることによって、重量平均分子量(Mw)が30,000~80,000であり、かつ結晶融解エンタルピー(ΔH)が10~30J/gであるエポキシ基及びパーオキサイド基を有する反応性重合体を得;前記反応性重合体を、アクリルアミドおよびアクリルアミド誘導体からなる群より選択される少なくとも一種の親水性単量体と反応させることによって、ブロック共重合体を製造し;さらに前記ブロック共重合体を前記基材層上に塗布することによって、潤滑層を前記基材上に形成することを有する、医療用具の製造方法。【選択図】なし