The present invention provides a zirconia sintered body containing a fluorescent agent, excellent in light transmittance and strength, a zirconia body obtained by the zirconia sintered body and a zirconia calcined material.The present invention relates toSintered zirconia containing fluorescent materialContains 4.5 to 9.0 mol% of yttriaThe crystal grain size is 180 nm or less.Zirconia sintered body with 3 point bending strength greater than 500 MPa；A zirconia molded body comprising a fluorescent agentContains 4.5 to 9.0 mol% of yttriaThe point bending strength after sintering for 1100 h under normal pressure was 500 MPa or more.A zirconia molded body with a particle size of less than 180 nm after sintering for 1100 hours under normal pressure；A zirconia calcite containing a fluorescent agent；Contains 4.5 to 9.0 mol% of yttriaThe point bending strength after sintering for 1100 h under normal pressure was 500 MPa or more.The present invention relates to a zirconia calcined material having a crystal grain size of 180 nm or less after sintering for 1100 hours under normal pressure.本発明は、蛍光剤を含み、透光性と強度に優れたジルコニア焼結体、該ジルコニア焼結体が得られるジルコニア成形体およびジルコニア仮焼体を提供する。本発明は、蛍光剤を含むジルコニア焼結体であって、イットリアを４．５～９．０モル％含み、結晶粒径が１８０ｎｍ以下であり、３点曲げ強さが５００ＭＰａ以上であるジルコニア焼結体；蛍光剤を含むジルコニア成形体であって、イットリアを４．５～９．０モル％含み、常圧下１１００℃で２時間焼結後の３点曲げ強さが５００ＭＰａ以上であり、常圧下１１００℃で２時間焼結後の結晶粒径が１８０ｎｍ以下であるジルコニア成形体；蛍光剤を含むジルコニア仮焼体であって、イットリアを４．５～９．０モル％含み、常圧下１１００℃で２時間焼結後の３点曲げ強さが５００ＭＰａ以上であり、常圧下１１００℃で２時間焼結後の結晶粒径が１８０ｎｍ以下であるジルコニア仮焼体に関する。