It contains a polymerizable monomer (A), a spherical particle (B) and a polymerization initiator (C) in an average primary particle diameter in the range of 230 nm to 1000 nm, and at least 90% of the individual particles constituting the spherical particle (B) A polymer obtained in the range of 5% before and after the average primary particle diameter, wherein the polymerizable monomer (A) and the spherical particle (B) are polymerized by the following formula (1): nP <；nF (nP is a polymerizable monomer (A)). Represents a refractive index at 25 ° C., nF represents a refractive index at 25 ° C. of the spherical particle (B), and satisfies the condition (X1). The ratio (Yb / Yw) of the Y value (Yb) of the measured color value by the Munsell colorimeter of the colored light under the black background and the measured value of the colored value by the Munsell colorimeter of the colored light under the white background was 0.2 to The curable composition which satisfy fills the range of 0.5 is provided.중합성 단량체(A), 평균 일차 입자 지름이 230nm~1000nm의 범위 내에 있는 구형 입자(B) 및 중합 개시제(C)를 함유하며, 구형 입자(B)를 구성하는 개개의 입자의 90% 이상이 평균 일차 입자 지름의 전후 5%의 범위에 존재하고, 중합성 단량체(A) 및 구형 입자(B)가 다음 식 (1): nP<；nF(nP는 중합성 단량체(A)를 중합하여 얻어지는 중합체의 25℃에서의 굴절률을 나타내고, nF는 구형 입자(B)의 25℃에서의 굴절률을 나타낸다.)로 표시되는 조건 (X1)을 만족하며, 두께 1mm의 경화체를 형성한 상태에서 각각 색차계를 이용하여 측정한, 흑색 배경하에서의 착색광의 먼셀 표색계에 의한 측색값의 Y값(Yb)과 백색 배경하에서의 착색광의 먼셀 표색계에 의한 측색값의 Y값(Yw)의 비(Yb/Yw)가 0.2~0.5의 범위를 만족하는 경화성 조성물을 제공한다.