Embodiments described herein relate to chemically and mechanically durable glass compositions and glass articles formed from the glass compositions. In one embodiment, the glass composition comprises about 70 mol% to about 80 mol% SiO2, about 3 mol% to about 13 mol% alkaline earth oxide, and X mol% Al2O3. And Y mol% alkali oxide. The alkali oxide may include Na2O in an amount greater than about 8 mol%. The Y:X ratio may be greater than 1 and the glass composition may be free of boron and boron compounds. In some embodiments, the glass composition may also be free of phosphorus and phosphorus compounds. A glass article formed from the glass composition may have at least class S3 acid resistance according to DIN 12116, at least class A2 base resistance according to ISO 695, and type HGA1 hydrolysis resistance according to ISO 720. .. [Selection diagram] None【課題】本明細書中に記載の実施形態は、化学的および機械的耐久性のあるガラス組成物およびこのガラス組成物から形成されたガラス物品に関する。【解決手段】１つの実施形態において、ガラス組成物は、約７０モル％～約８０モル％のＳｉＯ２と、約３モル％～約１３モル％のアルカリ土類酸化物と、Ｘモル％のＡｌ２Ｏ３と、Ｙモル％のアルカリ酸化物とを含み得る。アルカリ酸化物は、約８モル％超の量でＮａ２Ｏを含み得る。Ｙ：Ｘの比は１超であってよく、ガラス組成物はホウ素およびホウ素化合物を含んでいなくてもよい。一部の実施形態において、ガラス組成物は同様に、リンおよびリン化合物も含んでいなくてもよい。ガラス組成物から形成されたガラス物品は、ＤＩＮ１２１１６に準じた少なくともクラスＳ３の耐酸性、ＩＳＯ６９５に準じた少なくともクラスＡ２の耐塩基性、およびＩＳＯ７２０に準じたタイプＨＧＡ１の耐加水分解性を有し得る。【選択図】なし