The present invention provides a tissue-engineering porous calcium phosphate scaffold composition, and a method for producing a porous calcium phosphate scaffold composition by using a physical foaming scheme. To this end, a porous scaffold composition according to the present invention comprises: 45-58 wt% of calcium phosphate powder 40-50 wt% of one or more aqueous monomers selected from N-hydroxymethyl acrylamide and N,N-methylenebisacrylamide 0.6-1.5 wt% of polyoxyethyelene sorbitan monooleate 0.8-2 wt% of one or more anion surfactants selected from alkyl sulfate and alkyl ether sulfate and 0.2-0.5 wt% of a dispersing agent selected from polycarboxylic acid ammonium salt and polycarboxylic acid sodium salt.COPYRIGHT KIPO 2017본 발명은 조직공학용 다공성 인산칼슘 스캐폴드용 조성물 및 물리적인 발포법을 이용한 다공성 인산칼슘 스캐폴드 제조방법을 제공하기 위한 것이다.이에 본 발명에서는 인산칼슘 분말 45~58중량%와, 하이드록시메틸 아크릴아미드(N-Hydroxymethyl acrylamide), 메틸렌비스아크릴아미드(N,N-Methylenebisacrylamide) 중에서 선택되는 1종 이상의 수계 모노머 40~50중량%와, 폴리옥시에틸렌 소르비탄 모노올레에이트(Polyoxyethyelene Sorbitan Monooleate) 0.6~1.5중량%와, 알킬 설페이트(Alkyl sulfate)계, 알킬 에테르 설페이트(Alkyl ether sulfate)계 중에서 선택되는 1종의 음이온 계면활성제 0.8~2중량%와, 폴리카본산 암모늄염, 폴리카본산 나트륨염 중에서 선택되는 1종의 분산제 0.2~0.5중량%를 포함하여 조성되는 다공성 스캐폴드 조성물을 개시한다.