Disclosed is a method for preparing a surface coating with a reduced degradation rate of a biodegradable magnesium alloy vascular stent, comprising firstly grafting a silane coupling agent to the surface of a magnesium alloy by dip coating, heat curing, and forming a silane coupling agent coating on the surface of the magnesium alloy and then coating a polymer on the surface of the silane coupling agent coating by spin coating, and drying under vacuum to form a polymer coating. The polymer coating coated on the surface of the magnesium alloy and pretreated by a silane coupling agent can enhance the bonding force with the surface of the magnesium alloy vascular stent to suppress excessive degradation of the magnesium alloy matrix, and improve the biocompatibility of the vascular stent.Linvention concerne un procédé de préparation dun revêtement de surface à vitesse de dégradation réduite dun stent vasculaire en alliage de magnésium biodégradable, consistant tout dabord à greffer un agent de couplage silane sur la surface dun alliage de magnésium par revêtement par immersion, durcissement à chaud, et formation dun revêtement dagent de couplage silane sur la surface de lalliage de magnésium et à appliquer ensuite un polymère sur la surface du revêtement dagent de couplage silane par revêtement par centrifugation, et séchage sous vide pour former un revêtement polymère. Le revêtement polymère appliqué sur la surface de lalliage de magnésium et prétraité par un agent de couplage silane peut améliorer la force de liaison avec la surface du stent vasculaire en alliage de magnésium afin de supprimer une dégradation excessive de la matrice dalliage de magnésium, et daméliorer la biocompatibilité du stent vasculaire.