The present invention relates to an organopolysiloxane graft polymer which has an organopolysiloxane segment as the main chain, while having a polymer segment derived from an unsaturated monomer as a side chain, and wherein: the content of the organopolysiloxane segment in the organopolysiloxane graft polymer is from 35% by mass to 70% by mass (inclusive) and from 40% by mass to 90% by mass (inclusive) of a repeating unit derived from a nonionic unsaturated monomer having a glass transition temperature (Tg) of 60°C or more (excluding a repeating unit derived from an unsaturated monomer having an amino group) and from 10% by mass to 60% by mass (inclusive) of a repeating unit derived from a cationic unsaturated monomer are contained in the polymer segment derived from an unsaturated monomer.La présente invention concerne un polymère greffé à base dorganopolysiloxane comportant un motif organopolysiloxane en tant que chaîne principale et un motif polymère dérivé dun monomère insaturé en tant que chaîne latérale. La teneur en motif organopolysiloxane du polymère greffé à base dorganopolysiloxane varie de 35 à 70 % en poids (bornes incluses). Le motif polymère dérivé dun monomère insaturé comporte, quant à lui, de 40 à 90 % en poids (bornes incluses) dun motif structural dérivé dun monomère insaturé non ionique présentant une température de transition vitreuse (Tg) supérieure ou égale à 60 °C (à lexclusion de tout motif structural dérivé dun monomère insaturé comportant un groupe amine) et de 10 à 60 % en poids (bornes incluses) dun motif structural dérivé dun monomère cationique insaturé.主鎖としてオルガノポリシロキサンセグメントを有し、側鎖として不飽和単量体由来の重合体セグメントを有するオルガノポリシロキサングラフトポリマーであって、オルガノポリシロキサングラフトポリマー中における前記オルガノポリシロキサンセグメントの含有量が35質量%以上70質量%以下であり、前記の不飽和単量体由来の重合体セグメント中に、ガラス転移温度Tgが60℃以上の非イオン性の不飽和単量体由来の繰り返し単位(但しアミノ基を有する不飽和単量体由来の繰り返し単位を除く)を40質量%以上90質量%以下含み、更にカチオン性の不飽和単量体由来の繰り返し単位を10質量%以上60質量%以下含有する、オルガノポリシロキサングラフトポリマーに関する。