Manganese-cobalt (Mn-Co) spinel oxide nanowire arrays are synthesized at low pressure and low temperature by a hydrothermal method. The method can include contacting a substrate with a solvent, such as water, that includes Mn04- and Co2 ions at a temperature from about 60°C to about 120°C. The method preferably includes dissolving potassium permanganate (KMn04) in the solvent to yield the Mn04- ions. the substrate is The nanoarrays are useful for reducing a concentration of an impurity, such as a hydrocarbon, in a gas, such as an emission source. The resulting material with high surface area and high materials utilization efficiency can be directly used for environment and energy applications including emission control systems, air/water purifying systems and lithium-ion batteries.La présente invention concerne des réseaux de nanofils d'oxyde de spinelle de manganèse-cobalt (Mn-Co) synthétisés à basse pression et basse température par un procédé hydrothermique. Le procédé peut consister à mettre en contact un substrat avec un solvant, tel que de l'eau, qui comprend des ions Mn04 et Co2 à une température d'environ 60 °C à environ 120 °C. Le procédé consiste de préférence à dissoudre du permanganate de potassium (KMn04) dans le solvant pour produire les ions Mn04. Les nanoréseaux sont utiles pour réduire une concentration d'une impureté, telle qu'un hydrocarbure, dans un gaz, tel qu'une source d'émission. Le matériau obtenu ayant une surface élevée et une efficacité d'utilisation de matériaux élevée peut être directement utilisé pour des applications d'environnement et d'énergie comprenant des systèmes de commande d'émission, des systèmes de purification d'air/eau et des batteries au lithium-ion.