Provided is borosilicate glass for medical containers which is glass that does not include BaO, which has excellent chemical durability and hydrolysis-resistance, and which can maintain the excellent chemical durability and hydrolysis-resistance even after various thermal treatments during processing of the containers. The present invention is characterized by including, as essential components, SiO2, Al2O3, B2O3, and R2O (R is one type or more selected from Li, Na, and K), the content of CaO being 0 to less than 0.5 mol%, the value of (Na2O+K2O+Li2O-Al2O3)/B2O3 being 0.315 to 0.350 in molar ratio, and substantially not including BaO.L'invention concerne un verre de borosilicate pour des récipients médicaux, qui est un verre qui ne comprend pas de BaO, qui présente une excellente durabilité chimique et une excellente résistance à l'hydrolyse et qui peut maintenir l'excellente durabilité chimique et l'excellente résistance à l'hydrolyse, même après plusieurs traitements thermiques pendant le traitement des récipients. La présente invention est caractérisée en ce qu'elle comprend, comme constituants essentiels, SiO2, Al2O3, B2O3 et R2O (R est un ou plusieurs types choisis parmi Li, Na et K), la teneur en CaO étant de 0 à moins de 0,5 % en mole, la valeur de (Na2O+K2O+Li2O-Al2O3)/B2O3 étant de 0,315 à 0,350 en rapport molaire et ne comprenant pratiquement pas de BaO.ＢａＯを含有しないガラスであって、化学的耐久性や加水分解抵抗性が良好な、且つ容器加工時の種々の熱処理後も優れた化学的耐久性や加水分解抵抗性を維持することができる医薬容器用ホウケイ酸ガラスを提供する。ＳｉＯ２、Ａｌ２Ｏ３、Ｂ２Ｏ３、Ｒ２Ｏ（ＲはＬｉ、Ｎａ及びＫから選ばれる１種類以上）を必須成分として含むとともに、ＣａＯの含有量が０～０．５モル％未満、（Ｎａ２Ｏ＋Ｋ２Ｏ＋Ｌｉ２Ｏ－Ａｌ２Ｏ３）／Ｂ２Ｏ３の値がモル比で０．３１５～０．３５０、ＢａＯを実質的に含まないことを特徴とする。