PURPOSE: A surface treatment of medical implant and a technology of coating of biocompatible thin film are provided to prevent the nucleation of the calcium phosphate and to promote the formation of the calcium phosphate. CONSTITUTION: A surface treatment of medical implant and a technology of coating of biocompatible thin film include: a step of manufacturing PH 0.05-6.0 of acidic aqueous solution which has calcium ion, phosphate ion, and materials inhibiting the nucleus generation of calcium phosphate； a step of dipping the implant for half an hour to 100 hours； a step of reacting the mixed solution while increasing the temperature of the aqueous solution to 30-150 deg.C after adding alkaline aqueous solution to the aqueous solution and controlling it at pH 9.0 - 14.0； and a step of drying and washing the implant coated with calcium phosphate.본 발명은 임플란트 표면의 표면 거칠기를 증가시켜 생체 친화도를 높이고 생체 친화성 박막을 임플란트 표면에 코팅하는 방법에 대한 것으로, 보다 상세하게는 수용액상에서 임플란트의 표면 거칠기를 증가시키고 임플란트 표면에 인산칼슘 박막을 형성시키는 방법에 관한 것이다.본 발명은 수용액을 이용하여 임플란트 표면의 거칠기를 증가시키고 상온의 알칼리화된 수용액에서 인산칼슘의 핵생성이 이루어지지 않게 하고 수용액의 온도를 높여 인산칼슘의 형성을 촉진시키는 방법으로 임플란트 표면을 고순도의 인산칼슘의 초미립 결정으로 형성된 박막으로 이루어진 코팅층을 형성시키는 방법으로 제조 설비 및 공정이 단순한 경제적인 방법이다.