The proposed invention is intended to chemical compounds characterised by a porous structure, specifically, to producing calcium hydroxyapatite nano-crystals of the desired morphology intended for the treatment of skeletal disorders.The goal of the proposed invention is to obtain calcium hydroxyapatite nano-crystals of the desired morphology and size.The goal is achieved by preparing two solutions in the proposed method:a) 2.5-5.0wt% of calcium acetate and 1.2-2.4wt% of diammonium hydrogen tetroxo-phosphate is separately dissolved in 80-120 ml of distilled water and stir them at a temperature of 25-65 °C b) 1.15-2.25wt% of tartaric acid (TA) is dissolved in 90-100 ml of distilled water, and 4.4-8.8wt% of ethylenediaminetetraacetic acid (EDTA), 5.85-11.7wt% of 1,2- diaminocyclohexane-tetra-acetate (DCTA) is dissolved in 100 ml of water and 22 ml of 10% ammonia water solution, and stirred, pouring the solution b) into solution a), stirring for 15-20 hours at 65-75 °C, drying the obtained gel for 20-24 hours at 100 °C and, after it is grounded additionally heating for 5 hours at 900-1200 °C. By changing the molar ratios of the complex-forming reagents (DCTA, EDTA, and TA), it is possible to change the surface morphology of calcium hydroxyapatite.