Hypotubes for use with intra-corporal medical devices are fabricated from a stainless steel alloy exhibiting a combination of excellent yield strength with improved ductility as compared to cold worked AISI 304 stainless steel, from which hypotubes are typically fabricated. The stainless steel alloy may have: (1) a nitrogen content, a carbon content, or a combined nitrogen and carbon content that is greater than that allowed in AISI 304 stainless steel, providing an increased concentration of interstitial atoms to stabilize dislocations generated by cold work and/or (2) a combined nickel and manganese content that is lower than that allowed in AISI 304 stainless steel to reduce the stability of the austenitic structure, enabling a greater percentage of martensite to be stress-induced by a given level of cold work as compared to AISI 304 SS. Following cold working, the alloy may be heat treated to raise its yield strength by strain agingLa présente invention concerne des hypotubes destinés à être utilisés avec des dispositifs médicaux intracorporels, qui sont fabriqués à partir d'un alliage d'acier inoxydable présentant une combinaison d'une excellente limite d'élasticité avec une ductilité améliorée par comparaison à de l'acier inoxydable AISI 304 écroui à froid, à partir duquel on fabrique habituellement des hypotubes. L'alliage d'acier inoxydable peut avoir : (1) une teneur en azote, une teneur en carbone ou une teneur en azote et carbone combinés qui est supérieure à celle admise pour l'acier inoxydable AISI 304, donnant une concentration augmentée d'atomes interstitiels pour stabiliser des dislocations générées par un écrouissage à froid et/ou (2) une teneur en nickel et manganèse combinés qui est inférieure à celle admise pour l'acier inoxydable AISI 304 pour réduire la stabilité de la structure austénitique, permettant une induction selon la contrainte d'un pourcentage supérieur de martensite par un niveau donné d'écrouissage à froid par comparaison avec l'aci