PURPOSE: A partial straightening wire for teeth is provided to facilitate an irregular teeth correction by easily curving and transforming the wire.CONSTITUTION: A partial straightening wire for teeth is made of a shape memory alloy of which an austenite start temperature is between 30 and 45 deg C. The thickness of the wire is between 0.3 and 0.4 mm. The diameter of the wire is between 25 and 40 mm. The wire is rounded and wound. The wire is composed of 49.5-69.5 weight% of nickel, 29.5-49.5 weight% of titanium, 0.5-1.5 weight% of one or more of carbon, oxygen, nitrogen, manganese, silicon, cobalt, molybdenum, tungsten, vanadium, aluminum, zirconium, copper, tantalum, hafnium, silver, lead, bismuth, calcium, magnesium, tin, cadmium, zinc, antimony, strontium, sodium, arsenic, beryllium, barium, iron, niobium, boron, and chromium.COPYRIGHT KIPO 2013본 발명은 부분치열교정용 와이어에 관한 것으로, 부분치열교정용 와이어에 있어서, 상기 와이어는 30 ~ 45℃에서 오스테나이트 상으로 변태하는 형상기억합금으로 형성된다.본 발명에 따른 부분치열교정 와이어는 규격화가 되어있지 않아 어떤 형태의 교정치료에도 사용할 수 있고, 부분치열교정에 사용되고 남은 와이어의 부분을 버릴 필요가 없어 낭비를 줄일 수 있으며, 상기 와이어를 이루는 형상기억합금의 오르텐사이트로 변태되는 온도가 30 ~ 45℃이므로 치열교정시술중에 와이어가 오르텐사이트로 변태되지 않아 와이어의 굴곡과 변형이 쉬워 치열교정시술이 용이하다. 또한 시술자의 미세한 기술이 임상초기부터 적용될 수 있으므로 치열교정효과를 높여 치료기간을 단축할 수 있다.