PROBLEM TO BE SOLVED: To inexpensively provide a β type titanium alloy having a high melting point, easily producible since expensive Ta is not used, further, sufficiently considered with biocompatibility, and suitable as a bio-substitution material.SOLUTION: Provided is a β type titanium alloy comprising, by mass, above 20% to 45% Zr, 5 to 20% Nb and 1 to 5% Cr, and the balance Ti with inevitable impurities, and having a Youngs modulus of 100 GPa or lower. In the β type titanium alloy, since the Nb content is lower than that of the conventional titanium alloy, material cost is low, further, its Youngs modulus reaches 100 GPa or lower, and it is suitable as a bio-substitution material.SELECTED DRAWING: NoneCOPYRIGHT: (C)2016,JPO&INPIT【課題】高融点で高価なTaを使用しないために製造が容易であり、しかも生体適合性を充分に考慮に入れた、生体置換材料として好適なβ型チタン合金を安価に提供する。【解決手段】本発明のβ型チタン合金は、質量%で、Zr:20%超~45%、Nb:5~20%、Cr:1~5%、を含有し、残部がTiおよび不可避不純物からなり、ヤング率が100GPa以下であることを特徴とする。本発明のβ型チタン合金では、在来のチタン合金よりもNbの含有量が低いため、材料費が安く済む上、ヤング率が100GPa以下となり、生体置換材料として好適である。【選択図】なし