Provided is a method for manufacturing a functional bag for storing a corpse, which comprises: a first step of coating a cloth covering by soaking the cloth covering in 200 ppm of a silver nanocolloid solution a second strep of drying the coated cloth covering in a place away from direct sunlight a third step of soaking a cloth for an inner layer in a solution prepared by putting 10 g of 10,000 ppm of copper sulfate into 1 L of water and adding 50 g of a polysol bond, and then stirring the same a fourth step of drying the cloth for the inner layer in a place away from direct sunlight a fifth step of coating the dried cloth for the inner layer with a solution, which is prepared by putting 150 g of Kiyoseki stone into 1 L of water and stirring the same and then putting 100 g of 1,000 Mesh of seven stone powder and 70 g of the polysol bond, and then stirring for one hour, using a tentering machine for fiber processing, and drying the coated cloth a sixth step of manufacturing a primary corpse bag by sewing the cloth covering prepared in the second step and the cloth for the inner layer prepared in the fifth step so as to make into a shape of a bag with one opening and a seventh step of forming a pocket in one side of the cloth covering of the primary corpse bag and putting a zipper opening and closing the opening.COPYRIGHT KIPO 2016본 발명의 시체보관용 기능성 주머니의 제조방법은 200ppm 농도의 은나노콜로이드 용액에 외피용 천을 30분간 침지하여 상기 외피용 천을 코팅하는 제1 단계, 상기 코팅된 외피용 천을 직사광선이 차단된 공간에서 건조하는 제2 단계, 물 1L당 황산동 10,000ppm 10g을 투입하고 포리졸 접착제 50g을 첨가한 후 교반한 용액에 내피용 천을 30분간 침지하는 제3 단계, 상기 내피용 천을 직사광선이 차단된 공간에서 건조하는 제4 단계, 물 1L당 귀양석 150g 투입하고 교반한 후 칠보석 파우더 1,000Mesh 100g을 투입하고 포리졸 접착제 70g을 투입한 후 1시간 동안 교반한 용액을 섬유가공용 텐터기를 이용하여 상기 건조된 내피용 천에 도포 및 건조하는 제5 단계, 상기 제2 단계에서 제조된 외피용 천과 상기 제5 단계에서 제조된 내피용 천을 봉제하여 1개의 개구부가 형성된 주머니 형상으로 가공하여 제1차 사체주머니를 제조하는 제6 단계 및 상기 제1차 사체주머니의 외피용 천 일측에 포켓을 가공하고, 상기 개구부를 여닫는 지퍼를 설치하는 제7 단계를 포함하는 것을 특징으로 한다.