The present invention relates hyaluronate fiber, and more specifically, to hyaluronate fiber capable of being used in surgical suture, cosmetic filler, lifting thread, scaffold for tissue engineering, etc. According to the present invention, a method of manufacturing hyaluronate fiber by melt-spinning comprises the following steps: (a) adjusting the moisture content of hyaluronate with a molecular weight of 500 to 3,000 kDa within a range of 5 to 20%； (b) inserting the hyaluronate of which the moisture content is adjusted into a melt-spinning apparatus, heating the hyaluronate at 150 to 200C, and then performing spinning at high pressure to manufacture hyaluronate fiber； and (c) soaking the hyaluronate fiber in an aqueous ethanol solution to harden the surface thereof. According to the present invention, since the hyaluronate fiber is made of the hyaluronate as a main component, safety and biocompatibility are excellent. Moreover, the hyaluronate fiber is free from microorganism contamination when compared to general liquid hydrogel product, and is easy to be managed and used, and can thus be used as a material for tissue repair. Also, since the hyaluronate fiber is a solid type product, the volume is quite less with respect to the concentration of the hyaluronate, and thus can minimize pain and inconvenience of a patient when the hyaluronate fiber is injected inside the body, thereby maximizing curing effect.본 발명은 히알루론산염 파이버에 관한 것으로, 더욱 상세하게는 수술용 봉합사, 성형 필러, 리프팅용 실, 조직 공학용 세포지지체(Scaffold) 등으로 활용 가능한 히알루론산염 파이버 및 이의 제조방법에 관한 것이다.상기 용융 방사에 의한 히알루론산염 파이버의 제조방법은 (a) 분자량이 500~3,000kDa인 히알루론산염의 수분 함량을 5~20%로 조절하는 단계； (b) 수분 함량이 조절된 히알루론산염을 용융방사 장치에 넣고, 150~200℃로 가열 후, 고압방사하여 히알루론산염 파이버를 제조하는 단계； 및 (c) 히알루론산염 파이버를 에탄올 수용액에 침지시켜 표면을 경화시키는 단계를 포함한다.본 발명의 히알루론산염 파이버는 히알루론산염을 주성분으로 제조되어, 안전성(Safety) 및 생체 적합성이 뛰어날 뿐만 아니라, 통상의 액상 하이드로겔 제품과 달리 미생물 오염이 없고, 관리 및 사용이 쉬워서 다양한 형태의 조직 수복용 제제로 이용할 수 있다. 또한, 본 발명의 히알루론산염 파이버는 고체 형태의 제품이라 히알루론산염 농도 대비 체적 볼륨이 매우 작아 체내 투입 시 환자의 고통과 불편을