The present invention discloses water absorbent resin particles which have a 30-second value of DW under no pressure of 1.0 mL/g or more and a contact angle of 90 degrees or less as measured by a test that is carried out by the steps (i) and (ii) described below in this order. (i) Water absorbent resin particles and a liquid droplet are brought into contact with each other by dropping a spherical liquid droplet of 25% by mass saline having an equivalent diameter of 3.0 ± 0.1 mm on the surface of a layer that is formed of the water absorbent resin particles at 25 °C. (ii) The contact angle of the liquid droplet is measured at 30 seconds after the liquid droplet has come into contact with the surface.L'invention fournit des particules de résine absorbante qui présentent une valeur à 30 secondes de mouillabilité requise sans pression supérieure ou égale à １,０ｍＬ／ｇ, et un angle de contact, mesuré selon une expérience au cours de laquelle les points i) et ii) suivants sont effectués dans l'ordre, inférieur ou égal à 90 degrés. i) Des gouttes sphériques équivalentes à un diamètre de ３,０±０,１ｍｍ en termes de solution saline à 25% en masse sont déposées à la surface d'une couche constituée des particules de résine absorbante, à une température de 25°C, et les particules de résine absorbante et les gouttes sont ainsi mises en contact. ii) L'angle de contact des gouttes à un point dans le temps 30 secondes après le contact des gouttes avec la surface, est mesuré.無加圧ＤＷの３０秒値が、１．０ｍＬ／ｇ以上であり、以下のｉ）及びｉｉ）の順で行われる試験で測定される接触角が９０度以下である、吸水性樹脂粒子が開示される。ｉ）２５℃において、吸水性樹脂粒子からなる層の表面上に、２５質量％食塩水の直径３．０±０．１ｍｍに相当する球状液滴を滴下して、吸水性樹脂粒子と液滴とを接触させる。ｉｉ）液滴が表面に接触してから、３０秒後の時点の液滴の接触角を測定する。