This implant (1) is provided with a screw body (3) that comprises pure magnesium or a magnesium alloy and has a male screw (2), and an anodic oxide coating (4) that covers the outer surface of the screw body (3), wherein the male screw (2) has a clearance flank (21) that faces forward in the movement direction during screwing in of the screw body (3), and a pressure flank (22) that faces rearward in the movement direction, and the biodegradation period of an anodic oxide coating (41) on the clearance flank (21) is shorter than the biodegradation period of an anodic oxide coating (42) on the pressure flank (22).Linvention concerne un implant (1), qui est pourvu dun corps fileté (3), qui comprend du magnésium pur ou un alliage de magnésium et possède une vis mâle (2), et un revêtement doxyde anodique (4) qui recouvre la surface extérieure du corps de vis (3), la vis mâle (2) et un flanc de dégagement (21) dirigé vers lavant dans la direction du mouvement pendant le vissage du corps de vis (3), et un flanc de pression (22), dirigé vers larrière dans la direction du mouvement, et la période de biodégradation dun revêtement doxyde anodique (41) sur le flanc de dégagement (21) est plus courte que la période de biodégradation dun revêtement doxyde anodique (42) sur le flanc de pression (22).本発明のインプラント(1)は、純マグネシウムまたはマグネシウム合金からなり、雄ねじ(2)を有するねじ本体(3)と、該ねじ本体(3)の外表面を被覆する陽極酸化皮膜(4)とを備え、雄ねじ(2)が、ねじ本体(3)のねじ込み時に進行方向前方を向く遊び側フランク(21)と、進行方向後方を向く圧力側フランク(22)とを有し、遊び側フランク(21)上の陽極酸化皮膜(41)の生分解期間が、圧力側フランク(22)上の陽極酸化皮膜(42)の生分解期間よりも短い。