The present invention relates to: A dry implant composition consisting essentially of a mixture of nanocrystalline hydroxyapatite particles derived from natural bones of size 50-200 μm and fragments of naturally cross-linked fibrous collagen material through a 0.5 mm sieve, for collagen A dry implant composition having a hydroxyapatite w/w ratio of 1.8 to 4.5； Use of a dry implant composition for preparing an injectable aqueous implant formulation for use in reproducible oral tissues extruded through a tapering system and a gouge 18 (0.838 mm inner diameter) 25.4 mm long cannula Tapering system and 8 gouges (0.838 mm inside) with a force of 60 N or less, obtainable by rehydration and homogeneous mixing of sterile isotonic or sterile isotonic physiological saline and 25-45 w/w% of the dry implant composition Diameter) injectable aqueous implant formulation for use in oral tissue regeneration that can be extruded through a 25.4 mm long cannula； -A method for preparing the injectable aqueous implant formulation comprising re-hydration and homogeneous mixing of 20 to 20 dry implant compositions as defined above in sterile water or sterile isotonic physiological saline； -A kit for preparing said injectable aqueous implant formulation for use in oral tissue regeneration, comprising: Syringe with mixing device containing the dry implant 2 composition as defined above, a tapering system and a gouge 18 (0.838 mm inner diameter) 25.4 mm long cannula -A container filled with an appropriate amount of sterile water or sterile isotonic solution.본 발명은 하기에 관한 것이다:-크기가 50 내지 200 ㎛ 인 천연 골로부터 유래된 나노결정질 히드록시아파타이트 입자 및 0.5 ㎜ 체를 통과하는 자연적으로 가교결합된 섬유질 콜라겐 물질의 단편의 혼합물로 본질적으로 이루어진 건조 임플란트 조성물로서, 콜라겐에 대한 히드록시아파타이트의 w/w 비가 1.8 내지 4.5 인 건조 임플란트 조성물；-테이퍼링 시스템 및 가우지 18 (0.838 ㎜ 내부 직경) 25.4 ㎜ 길이 캐뉼라를 통해 압출가능한 구강 조직 재생에서 사용하기 위한 주사가능한 수성 임플란트 제형을 제조하기 위한, 건조 임플란트 조성물의 용도-재수화 및 멸균수 또는 멸균 등장성 생리 식염수와 25-45 w/w % 의 상기 건조 임플란트 조성물의 균일한 혼합에 의해 수득가능한, 60 N 이하의 힘으로 테이퍼링 시스템 및 8 가우지 (0.838 ㎜ 내부