[Problem] To provide a cross - copolymer excellent in terms of flexibility, tensile property, transparency, and blocking resistance and a medical single-layer tube.[Solution] A cross - copolymer which comprises: 75-95 mass% main chains of an aromatic vinyl/olefin copolymer made up of 8.99-15.99 mol% units of an aromatic vinyl monomer, 84-91 mol% units of an olefin monomer, and 0.01-0.5 mol% units of an aromatic polyene monomer； and 5-25 mass% cross - chains of a polymer made up of units of an aromatic vinyl monomer. When examined in a nitrogen gas stream of 30 mL/min by a DCS method in which the cross - copolymer is cooled to -50ºC, subsequently heated to 180ºC at a heating rate of 10 ºC/min, cooled again to -50ºC, and heated to 180ºC at a heating rate of 10 ºC/min, then the cross - copolymer has a fusion peak top temperature of 60-80ºC and a heat of fusion of 45-75 J/g, the heat of fusion being calculated from the area surrounded by a straight line drawn between the -20ºC and 130ºC points of the DSC curve and by the DSC curve between -20ºC and 130ºC.Le problème à résoudre par la présente invention est de fournir un copolymère réticulé qui présente d'excellentes propriétés de flexibilité, de résistance à la traction, de transparence et de résistance à l'obstruction, ainsi qu'un tube monocouche médical. La solution de l'invention consiste en un copolymère réticulé qui comprend : de 75 à 95 % en masse de chaînes principales d'un copolymère d'oléfine et de vinyle aromatique constitué de 8,99 à 15,99 % en moles de motifs de monomère vinylique aromatique, de 84 à 91 % en moles de motifs d'un monomère oléfinique et de 0,01 à 0,5 % en moles de motifs d'un monomère de polyène aromatique ； et de 5 à 25 % en masse de chaînes transversales d'un polymère constitué de motifs d'un monomère vinylique aromatique. Lorsqu'il est examiné dans un courant d'azote gazeux de 30 mL/min par un procédé DCS dans lequel le copolymère réticulé est refroidi à -50 °C, puis chauffé à 180 °C à un