An embolic coil to which an Au-Pt alloy wire is applied, which has good shape stability. The present invention relates to an embolization coil composed of a wire material made of an Au-Pt alloy, wherein the wire material constituting the embolization coil has a Pt concentration of 24 mass% or more and less than 34 mass%, and the balance Au. The α-phase matrix has a material structure in which a Pt-rich phase made of an Au—Pt alloy having a Pt concentration of 1.2 to 3.8 times the Pt concentration of the α phase is distributed in the α phase matrix. The wire has a volume magnetic susceptibility of −13 ppm or more and −5 ppm or less, and the wire has an average crystal grain size of 2 or more measured by a line segment method in a material structure of a cross section in the short direction. The embolization coil has an average value of 0.20 μm or more and 0.35 μm or less. [Selection] Figure 3【解決課題】Ａｕ－Ｐｔ合金線材を適用した塞栓用コイルであって、形態安定性が良好なものを提供する。【解決手段】本発明は、Ａｕ－Ｐｔ合金からなる線材で構成された塞栓用コイルであって、前記塞栓用コイルを構成する前記線材は、Ｐｔ濃度２４質量％以上３４質量％未満、残部Ａｕの組成を有し、α相マトリックスに、α相のＰｔ濃度に対して１．２～３．８倍のＰｔ濃度のＡｕ－Ｐｔ合金からなるＰｔリッチ相が分布した材料組織を有しており、前記線材は、その体積磁化率が－１３ｐｐｍ以上－５ｐｐｍ以下であり、更に、前記線材は、その短手方向断面の材料組織において、線分法により測定された２以上の平均結晶粒径の平均値が０．２０μｍ以上０．３５μｍ以下となる、塞栓用コイルである。【選択図】図３