A sulfate esterified cellulose fiber having a cellulose type I crystal structure is provided. The chemically modified cellulose fiber which has a cellulose I-type crystal crystallization, and the hydroxyl group of cellulose was substituted by the substituent represented by Formula (1), The introduction amount of a substituent is 0.1-3.0 mmol / g of chemical-modified cellulose fibers, and averages It is a chemically modified cellulose fiber whose polymerization degree is 350 or more (However, M shows a 1-3 trivalent cation in Formula (1).). In the production of the chemically modified cellulose fibers, sulfamic acid and cellulose fine fibers as constituents of the cellulose fibers are reacted by treating the cellulose fibers with sulfamic acid while maintaining the cellulose fiber shape.셀룰로오스 I 형 결정 구조를 갖는 황산에스테르화 셀룰로오스 섬유를 제공한다. 셀룰로오스 I 형 결정을 갖고, 셀룰로오스의 수산기의 일부가, 식 (1) 로 나타내는 치환기에 의해 치환된 화학 수식 셀룰로오스 섬유로서, 치환기의 도입량이 화학 수식 셀룰로오스 섬유 1 g 당 0.1 ∼ 3.0 m㏖ 이고, 평균 중합도가 350 이상인, 화학 수식 셀룰로오스 섬유이다 (단, 식 (1) 중, M 은 1 ∼ 3 가의 양이온을 나타낸다). 그 화학 수식 셀룰로오스 섬유를 제조할 때에는, 셀룰로오스 섬유 형상을 유지한 채로 셀룰로오스 섬유를 술파민산으로 처리함으로써, 술파민산과 당해 셀룰로오스 섬유의 구성 요소인 셀룰로오스 미세 섬유를 반응시킨다.