The present invention provides a method for producing a powder containing zirconia particles and a fluorescent agent, which can easily manufacture a zirconia sintered body having both high light transmittance and high strength, despite including a fluorescent agent. The present invention, as a method for producing a powder containing zirconia particles and a fluorescent agent, a mixing step of mixing the slurry containing the zirconia particles and the fluorescent agent in the liquid state, and drying to dry the slurry containing the zirconia particles and the fluorescent agent It is related with the manufacturing method which has a process. The fluorescent agent contains a metal element, and the content of the fluorescent agent in the powder is preferably 0.001 to 1 mass% in terms of oxide of the metal element relative to the mass of zirconia, and the average primary particle diameter of the zirconia particles is 30 nm It is preferable that it is the following, and it is preferable that zirconia particle contains yttria 2.0-9.0 mol%.본 발명은, 형광제를 포함함에도 불구하고, 높은 투광성 및 높은 강도를 겸비한 지르코니아 소결체를 간편하게 제조할 수 있는, 지르코니아 입자 및 형광제를 포함하는 분말의 제조 방법을 제공한다. 본 발명은, 지르코니아 입자 및 형광제를 포함하는 분말의 제조 방법으로서, 지르코니아 입자를 포함하는 슬러리와 액체 상태의 형광제를 혼합하는 혼합 공정과, 지르코니아 입자 및 형광제를 포함하는 슬러리를 건조시키는 건조 공정을 갖는, 제조 방법에 관한 것이다. 형광제는 금속 원소를 포함하고, 상기 분말에 있어서의 형광제의 함유량이 지르코니아의 질량에 대하여 금속 원소의 산화물 환산으로 0.001 ∼ 1 질량％ 인 것이 바람직하고, 지르코니아 입자의 평균 1 차 입자경은 30 ㎚ 이하인 것이 바람직하고, 지르코니아 입자는 이트리아를 2.0 ∼ 9.0 몰％ 포함하는 것이 바람직하다.