A process for making foamed glasses and ceramics from sol-gels is disclosed. The method includes preparing a mixture of reactants capable of forming a sol-gel with addition of a catalyst to control the condensation stage followed by foaming using vigorous agitation in the presence of surfactants. The gelled bodies are aged, dried, and thermally stabilized to obtain a consolidated macroporous material. The resulting structure comprises a three-dimensional network of spherical open pores that are thoroughly interconnected. The process may involve sol-gel systems using a mixture of metal alkoxides, and may produce glasses in unary systems (SiO2), binary systems (70% mol SiO2-30% mol CaO), and ternary systems (60% mol SiO2, 36% mol CaO, 4% mol P2O5). The macroporous material has pores in the 10-500 µm range and has potential for use as matrix in tissue engineering, in bone repair, and in organ regeneration.Linvention concerne un procédé de fabrication de verres et de céramiques expansés à partir de sol-gels. Le procédé consiste à préparer un mélange de réactifs capables de former un sol-gel avec laddition dun catalyseur de façon à réguler le stade de condensation suivi dexpansion par un brassage vigoureux en présence de tensioactifs. Les corps gélifiés sont vieillis, séchés et thermiquement stabilisés de façon à obtenir un matériau macroporeux consolidé. La structure résultante comporte un réseau tridimensionnel de pores ouverts sphériques complètement interconnectés. Le procédé, qui peut impliquer des systèmes sol-gel par un mélange dalcoxydes métalliques, peut produire des verres en systèmes unaires (SiO2), binaires (70 %mol SiO2-30 % mol CaO), et ternaires (60 % mol SiO2, 36 % mol CaO, 4 % mol P2O5). Le matériau macroporeux, doté de pores dans la gamme de 10-500 νm, peut être utilisé comme matrice en génie tissulaire, en réparation osseuse et en régénération dorganes.