A novel method for manufacturing bone regenerating material containing calcium phosphate particles in biodegradable fiber made of PLGA with commercial efficiency using electrospinning and a new bone regenerating material produced by the method Is required. The PLGA resin was heated in a kneader so that the viscosity of the resin was 102~Ten7Pa s and the powders of calcium phosphate fine particles are introduced while rotating the blades of the kneader so as to mix the powder with the softened PLGA resin and continuously rotate the blades of the kneader in the heating state , The mixture is thermally and mechanically kneaded to disintegrate the aggregation of the calcium phosphate fine particles to prepare a composite in which fine particles of calcium phosphate are dispersed in the PLGA resin, Is dissolved in a solvent and agitated for a predetermined time to prepare a spinning solution in which the PLGA resin is completely dissolved with the solvent and the calcium phosphate fine particles are dispersed without agglomeration in the solution in which the PLGA resin is dissolved and the spinning solution , The calcium phosphate fine particles are dispersed substantially uniformly in the biodegradable fiber To produce a biodegradable fiber.PLGAからなる生分解性繊維にリン酸カルシウム粒子を含有させた骨再生用材料をエレクトロスピニングを用いて商業的効率性をもって製造するための新たな方法、およびその方法で製造された新たな骨再生用材料が求められている。 PLGA樹脂をニーダー中で加熱して、樹脂の粘度が102~107Pa・sになるまで軟化させ、リン酸カルシウム微粒子の粉体をニーダーの羽根を回転させながら投入することによって、粉体を軟化したPLGA樹脂と混合し、ニーダーの羽根を前記加熱状態で継続して回転させることによって前記混合物に対して熱的かつ機械的エネルギーをかけて混練し、リン酸カルシウム微粒子の凝集を解砕することによって、リン酸カルシウムの微粒子がPLGA樹脂中に分散した複合体を作製し、前記複合体を溶剤で溶かし、所定時間撹拌することによって、PLGA樹脂が溶剤によって完全に溶解され、かつリン酸カルシウム微粒子がPLGA樹脂が溶解された溶液中で凝集することなく分散した紡糸溶液を作製し、当該紡糸溶液を用いてエレクトロスピニングすることによって、リン酸カルシウム微粒子が生分解性繊維中に略均一に分散している生分解性繊維を製造する。