The present invention relates to a self-supporting interface dressing formed from a thin layer of a composition comprising a hydrophobic matrix and having through holes. According to the invention, this hydrophobic matrix comprises: per 100 parts by weight of a styrene-saturated olefin-styrene triblock copolymer having a viscosity between 0.2 and 2 Pa.s, as measured in a 10% (weight/weight) solution in toluene； from 400 to 1220 parts by weight of a plasticizer, preferably a plasticizing oil； and from 0 to 720 parts by weight of petroleum jelly； it being specified moreover that: the total amount of plasticizer and petroleum jelly is greater than or equal to 750 parts by weight； the amount of petroleum jelly is between 400 and 720 parts by weight when the amount of plasticizer is between 1000 and 1220 parts by weight. Application: treatment of woundsLa présente invention concerne un pansement interface autoporté formé d'une couche mince d'une composition comprenant une matrice hydrophobe et comportant des trous traversants. Selon l'invention, cette matrice hydrophobe comprend； pour 100 parties en poids d'un copolymère tribloc styrène-oléfine saturée-styrène présentant une viscosité comprise entre 0,2 et 2 Pa.s, telle que mesurée dans une solution à 10 % (masse/masse) dans le toluène； de 400 à 1 220 parties en poids d'un plastifiant, de préférence une huile plastifiante； et de 0 à 720 parties en poids de vaseline； étant en outre précisé que； la quantité totale de plastifiant et de vaseline est supérieure ou égale à 750 parties en poids； la quantité de vaseline est comprise entre 400 et 720 parties en poids lorsque la quantité de plastifiant est comprise entre 1 000 et 1 220 parties en poids. Application : traitement des plaies