JUNG, IN IL,정인일,KIM, SEONG SOO,김성수,KIM, YU HWAN,김유환,JUNG, IN ILKR,KIM, SEONG SOOKR,KIM, YU HWANKR
申请号：
KR1020170006960
公开号：
KR1020180084217A
申请日:
2017.01.16
申请国别(地区):
KR
年份:
2018
代理人:
摘要：
The present invention relates to a method for coating a 3D printed implant capable of preventing cytotoxicity of the 3D printed implant by performing surface passivation and surface processing, and evenly coating a surface including the inside of a lattice structure when the 3D printed implant is printed by a lamination structure of metal powder, and includes the lattice structure. According to an embodiment of the present invention, the method for coating a 3D printed implant comprises: a printing step (S10) of manufacturing the implant having the lattice structure based on 3D printing； a step (S20) of injecting a precursor of a steam state in a predetermined chamber in which the implant is stored； a step (S30) of depositing the injected precursor on a surface of the lattice structure； a step (S40) of injecting inert gas to the chamber； a step (S50) of allowing the injected inert gas to remove a precursor which is not deposited； a step (S60) of injecting an oxidizer of a steam state to the chamber； and a step (S70) of forming a titanium oxide by responding the injected oxidizer to the precursor which is deposited on the lattice structure.본 발명의 일 실시예에 의하면, 표면 패시베이션 및 표면 처리를 함으로써 3D 프린팅된 임플란트의 세포독성을 방지할 수 있으며, 3D 프린팅된 임플란트가 금속분말의 적층구조로 프린팅되어 격자구조를 갖는 경우 격자구조 내부를 포함한 표면 전체를 골고루 코팅할 수 있는 효과가 있다. 이를 위해 특히 본 발명의 일 실시예는, 3D 프린팅에 기반하여 격자구조를 갖는 임플란트를 제조하는 프린팅 단계(S10)； 임플란트가 수용된 소정 챔버에 증기 상태의 전구체를 주입하는 단계(S20)； 주입된 전구체가 격자구조 표면에 증착되는 단계(S30)； 챔버에 불활성 가스를 주입하는 단계(S40)； 주입된 불활성 가스가 전구체 중 증착되지 않은 전구체를 제거하는 단계(S50)； 챔버에 증기 상태의 산화제를 주입하는 단계(S60)； 및 주입된 산화제가 격자구조에 증착된 전구체와 반응하여 티타늄 옥사이드를 형성하는 단계(S70)를 포함할 수 있다.