Iron-platinum ferromagnetic particles can be dispersed in a polymer and coated in or on a medical device or directly connected to or embedded in a medical device and magnetized It was discovered. By using a magnetized device, magnetically labeled cells are attracted, captured and / or retained on the surface of the device in vivo. These magnetic particles have an iron / platinum core. Annealing of the Fe / Pt particles is very important to guide the L10 internal crystal phase. The Fe: Pt molar ratio for forming the crystalline phase is important and a molar range of 1.2 to 3.0 Fe (molar precursor, i.e. starting compound) relative to Pt is desirable for magnetization. The overall magnetic force can be measured using a “superconducting quantum interference device” which is a high sensitivity magnetometer. The total magnetic force is in the range of 0.1 to 2.0 Tesla.鉄－白金強磁性粒子が、ポリマー中に分散され、医療用デバイス中もしくは医療用デバイス上にコーティングされるかまたは医療用デバイスに直接連結されるかまたは医療用デバイスに包埋され、磁化され得ることが発見された。磁化されたデバイスを用いることにより、磁気により標識された細胞がインビボにおいてそのデバイスの表面上に引きつけられ、捕捉され、そして／または保持される。それらの磁性粒子は、鉄／白金コアを有する。そのＦｅ／Ｐｔ粒子の焼きなましは、Ｌ１０内部結晶相を導くために非常に重要である。その結晶相を形成するためのＦｅ：Ｐｔモル比は重要であり、Ｐｔに対して１．２～３．０のＦｅというモル範囲（モル前駆体、すなわち出発化合物）が磁化にとって望ましい。全体としての磁力は、高感度磁力計である「超伝導量子干渉素子」を用いて計測され得る。全磁力は、０．１～２．０テスラの範囲内である。