The present invention relates to a biodegradable polymer film and a method for producing a biodegradable polymer film. More particularly, the present invention relates to a biodegradable polymer film which is irradiated with a light source of 100 to 400 kGy and has a crosslinking density of 150 to 2200 mol / m The present invention provides a biodegradable polymer film and a method for producing the biodegradable polymer film, and also provides a medical use as a hydrogel and its adhesion preventive film prepared by swelling the biodegradable polymer film with a solvent. According to the present invention, the biodegradable polymer film having increased cross-linking density by increasing the irradiation dose of the light source has high tensile strength and fracture elongation, and has good physical properties as an anti-adhesion film. Also, the synthesized PEGDC has very low cytotoxicity, Since the gel film is completely decomposed in the body after 3 weeks, it can be used safely in the body and can be usefully used as a material for adhesion preventive film, wound dressing, mask pack and the like.본 발명은 유착방지막 용도의 생분해성 고분자 필름 및 생분해성 고분자 필름의 제조 방법에 관한 것으로, 보다 상세하게는 생분해성 고분자 필름에 100 내지 400 kGy인 광원을 조사하여 가교 밀도가 150 내지 2200 mol/m3인 생분해성 고분자 필름과 이의 제조방법을 제공하며, 또한 상기 생분해성 고분자 필름을 용매로 팽윤시켜 제조한 하이드로겔과 이의 유착 방지막으로서의 의학적 용도를 제공한다.본 발명에 따르면, 광원의 조사량을 증가시켜 가교 밀도를 증가시킨 생분해성 고분자 필름은 높은 인장강도와 파단신장율을 보여 유착방지막으로써 좋은 물성을 가지며, 또한 합성된 PEGDC은 세포독성이 매우 적고 가교된 PEO 겔 필름은 3주 이후에 완전히 체내에서 분해되므로 체내에서도 안전하게 사용할 수 있어 유착 방지막, 창상 피복제, 마스크팩 등의 소재로서 유용하게 사용할 수 있다.