Disclosed is a method for preparing an air purification material. The method comprises the following steps: (1) a glass fibre is added to an ultra-high molecular weight polyethylene, and after stirring at an ultra-high speed, a cross-linking agent is added, and stirred again until uniform to obtain a mixture and (2) an active carbon powder is added to the above-mentioned mixture, and stirred until uniform, and then extrusion moulded at a temperature of 180°C-230°C and under a pressure of 500 MPa-3000 MPa. Also disclosed is an air purification material prepared by the above-mentioned preparation method. The air purification material has an excellent adsorbability for particles in air, and at the same time has a relatively good eliminating effect on automobile exhausts, bacteria, heavy metals and the like in air. The air purification material of the present invention is low in production difficulty, high in yield and good in purification effect, and has good application prospects in the aspect of outdoor air purification.Linvention concerne un procédé de préparation dune matière de purification de lair. Le procédé comprend les étapes suivantes : (1) une fibre de verre est ajoutée à un polyéthylène de poids moléculaire ultra-élevé, et après agitation à une vitesse ultra-élevée, un agent de réticulation est ajouté et le mélange de nouveau agité jusquà obtenir un résultat uniforme et (2) une poudre de charbon actif est ajoutée au mélange mentionné ci-dessus, le tout est agité jusquà obtenir un résultat uniforme, et est ensuite moulé par extrusion à une température comprise entre 180 °C et 230 °C et sous une pression de 500 MPa à 3 000 MPa. Linvention concerne également une matière de purification de lair préparée par le procédé de préparation susmentionné. La matière de purification de lair présente une excellente adsorbabilité pour les particules présentes dans lair, et en même temps a un effet délimination relativement bon sur les gaz déchappement des véhicules automo