The invention relates to a process for preparing a porous nanohydroxyapatite sustained release gel. The hydroxyapatite composite microspheres prepared by the method of the invention exhibit a uniform size distribution, the particle size distribution range is 10 to 100 µm, and the central particle diameter is 20 to 60 µm. Adding organic phase in the mixing process can effectively improve the stability of the suspension. the produced microsphere size is evenly distributed, and the particle size is larger than the microsphere size obtained by the traditional spray drying system, it can be used as a support material in the injection； The microsphere has a good shape with large pores which can improve material injection by speeding up drug metabolism time and maintaining stable and effective drug concentration in the body with better drug delivery.L'invention concerne un procédé de préparation d'un gel à libération prolongée à nanohydroxyapatite poreux. Les microsphères composites d'hydroxyapatite préparées par le procédé de l'invention présentent une distribution de taille uniforme, la plage de distribution de taille de particule est de 10 à 100 µm et le diamètre de particule central est de 20 à 60 µm. L'ajout de phase organique dans le processus de mélange peut effectivement améliorer la stabilité de la suspension. la taille de microsphère produite est répartie uniformément et la taille de particule est plus grande que la taille de microsphère obtenue par le système traditionnel de séchage de pulvérisation, cela peut être employé comme matériel de support dans l'injection ； la microsphère possède une bonne forme avec des pores élevés qui peuvent améliorer l'injection de matériaux en permettant d’accélérer le temps de métabolisme du médicament et de maintenir la concentration de médicament stable et efficace dans le corps avec une meilleure administration de médicaments.