摘要：
PURPOSE: A manufacturing method of a hemp microcrystalline cellulose is provided to manufacture a microcrystalline cellulose with a hemp stem cellulose having a specific molecular weight, an electric conductivity, an absorbing performance, an absorbing ability, a surface area, a granularity, and a particle size.CONSTITUTION: A manufacturing method of a hemp microcrystalline cellulose comprises a step of pulverizing a hemp stem raw material, low concentration alkali-treat the raw material or adding water into the raw material, and conducting a delignification by a heat treatment heating the mixture a step of acid-treating the delignified material and a step of neutralizing, washing, drying, and pulverizing the acid-treated raw material. The hemp microcrystalline cellulose has a high specific surface area and high adsorption ability and has a polymerization degree of about 150.COPYRIGHT KIPO 2013본 발명은 전통적으로 직물산업에 이용되고 있는 헴프(대마)를 대상으로 헴프 미세결정셀룰로오스(microcrystalline cellulose) 제조 방법에 관한 것으로, 헴프 부산물인 줄기를 가성소다를 처리한 후 진한 황산으로 분해시켜 미세결정셀룰로오스를 얻는 단계, 물리적 처리 방법인 폭쇄 전처리 후 황산 처리로 미세결정셀룰로오스를 얻는 단계를 포함하고 있다. 조건을 달리한 가성소다 처리와 폭쇄 처리(200℃, 300psi)는 헴프 줄기에 포함되어 있는 리그닌질을 제거하는 효과가 있으며, 황산 처리 농도 및 조건에 따라 헴프 줄기 셀룰로오스가 특정한 분자량,전도도, 흡수능, 흡유능, 비표면적, 입도 및 입자 크기를 가지는 미세결정셀룰로오스를 제조할 수 있다.