PROBLEM TO BE SOLVED: To provide a deodorant agent for a human body, providing good feeling in use and having high deodorant effects.SOLUTION: The deodorant agent for the human body contains fine particle-shaped silica gel including zinc oxide fine particles produced by a production method including a micronized silica hydrogel slurry-preparing step comprising a hydrothermal pulverizing step for forming slurry of the micronized silica hydrogel having an average particle diameter of &le100 &mum by subjecting silica hydrogel in a slurry state having SiO2 concentration of 5.0-15.0 mass% to hydrothermal treatment under stirring a mixed slurry-forming step for obtaining mixed slurry of the silica hydrogel fine particles and the zinc oxide fine particles by introducing the zinc oxide fine particles in a primary particle state having an average particle diameter of 0.1-0.5 &mum into the micronized silica hydrogel slurry and a drying step for drying the mixed slurry.COPYRIGHT: (C)2010,JPO&INPIT【課題】使用感触が良好で、かつ、消臭効果が高い人体用デオドラント剤の提供。【解決手段】本発明の人体用デオドラント剤は、シリカヒドロゲルを、SiO2 濃度が5.0質量%~15.0質量%のスラリー状態で、攪拌下水熱処理し、平均粒子径が100μm以下の微細化シリカヒドロゲルのスラリーとする水熱微粉砕工程を含む微細化シリカヒドロゲルスラリーの調製工程と、前記微細化シリカヒドロゲルスラリー中に平均粒子径が0.1μm~0.5μmで一次粒子状の酸化亜鉛微粒子を導入し、シリカヒドロゲル微粒子と前記酸化亜鉛微粒子との混合スラリーを得る混合スラリー化工程と、前記混合スラリーを乾燥する乾燥工程と、を含む製造方法により製造された、前記酸化亜鉛微粒子を内包する微粒子状シリカゲルを含むことを特徴とする。【選択図】なし