The present invention provides a method for preparing a high-silver-content zirconium phosphate powder, characterized in that same comprises: dispersing in an organic solvent a mesoporous zirconium phosphate powder and a polythiol compound, and subjecting same to ultrasonic dispersion for 0.5-2 hours adding silver nitrate and stirring for 12-24 hours, then using a spray drying method to remove the organic solvent, and placing the obtained powder into an environment of 800-1200°C and calcining for 1-6 hours to obtain a zirconium phosphate powder having a silver mass content of 3-8%. The polythiol compound in the present invention may effectively disperse into the holes of the zirconium phosphate and onto its surface, and the thiol group first bonds with the hydroxyl on the surface of the zirconium phosphate upon adding silver nitrate, the unreacted thiol group may effectively bond to silver ions, thus causing a large amount of silver ions to enter the mesopores of the zirconium phosphate and bond to the surface of the zirconium phosphate, forming high-silver-content zirconium phosphate particles.La présente invention concerne un procédé pour préparer une poudre de phosphate de zirconium à teneur élevée en argent, caractérisé en ce quil comprend : disperser, dans un solvant organique, une poudre de phosphate de zirconium mésoporeuse et un composé de polythiol, et les soumettre à une dispersion à ultrasons pendant 0,5 à 2 heures ajouter du nitrate dargent et agiter pendant 12 à 24 heures, puis utiliser un procédé de séchage par pulvérisation pour éliminer le solvant organique, et placer la poudre obtenue dans un environnement de 800 à 1 200 °C et calciner pendant 1 à 6 heures pour obtenir une poudre de phosphate de zirconium ayant une teneur massique en argent de 3 à 8 %. Le composé de polythiol selon la présente invention peut se disperser efficacement dans les trous du phosphate de zirconium et sur sa surface, et le groupe thiol se lie dabord à lhydroxyle sur la sur