As a major antifouling agent for bottom paints, the world-recognized problem of copper pyrithione has been to formulate products that control the elution from the coating film and lengthen the duration of the antifouling effect from the viewpoint of protecting the marine environment There are two ways to develop products with low particle size to develop them and to increase safety at the work site. The inventors of the present invention have found that by using a composite salt of an inorganic copper (II) salt and an inorganic ammonium salt instead of an inorganic copper (II) salt which is a raw material of a copper pyrithione conventional production method, It succeeded in obtaining a copper pyrithione aggregate composed of columnar, flat-plate particles. As a result, copper pyrithione aggregate particles having an average particle size in the range of 5.5 to 9 μm, mainly having a spherical shape and an ellipsoidal shape, can control the elution from the bottom antifouling coating film into seawater and the risk of dust inhalation The present invention solves the above-mentioned problems.주요한 선저도료용 방오제로서, 세계적으로 인지되어온 구리피리티온의 앞으로의 과제로는, 해양 환경 보호의 관점에서, 어떻게 도막으로부터의 용출을 제어하고, 방오 효력의 지속기간을 길게하는 형상의 제품을 개발하는가, 또 작업 현장에서의 안전성을 높이기 위해, 어떻게 미립이 적은 입자의 제품을 개발하는가 라는 두가지가 있었다. 본 발명자는, 구리피리티온 종래 제법의 원료인 무기구리(Ⅱ)염 대신에, 무기구리(Ⅱ)염과 무기암모늄염과의 복합염을 이용함으로써, 종래의 구리피리티온의 침상결정과 다른 작은 원주상, 평판상 입자로 이루어진 구리피리티온 집합체를 얻는 데에 성공했다. 이 결과, 주로 구형, 타원형을 갖는 5.5 - 9μm 미만의 범위의 평균 입자경의 구리피리티온 집합체 입자가 선저방오도막으로부터 해수에의 용출을 제어할 수 있는 것, 또한 작업 현장에서의 분진 흡입의 위험을 경감할 수 있는 것을 견출하여, 상기 과제를 해결하였다.