The present invention relates to a multicolored biodegradable mulching film for cultivating a sweet potato. The mulching film comprises 5-15 parts by weight of polylactic acid (PLA), 55-85 parts by weight of thermoplastic starch (TPS), 5-15 parts by weight of calcium, and 5-15 parts by weight of powder ceramics having a particle size of 200-600 mesh. A non-colored intermediate part having a width of 25-35 cm in a longitudinal direction and having longitudinally penetrated penetration holes at intervals of 20 cm or larger is formed, and both black edge parts are formed in parts excluding the intermediate part. The film is extruded at 110-130C in a blown film molding device, and a synthetic resin such as low density polyethylene (LDPE) is not used at all, so the film, when being buried in a soil, is completely bio-degraded by the metabolism of microorganisms. Environmental hormones and toxic gases are not discharged, and a composition dissolving temperature is low, so process time is reduced. Since the film has the non-colored intermediate part and the black edge parts, the film is suitable in cultivating a sweet potato. Also, the film includes calcium, so the film, when being left in an acid soil, modified the acid soil. Moreover, the film supplies nutrients of calcium to a plant or a fruit.본 발명은 고구마 재배용 배색 생분해성 멀칭필름에 있어서, 상기 멀칭필름은 폴리유산(PLA) 5~15중량부, 열가소성 전분(TPS) 55~85중량부, 칼슘 5~15중량부 및 입도 200~600메쉬(mesh)의 분말 세라믹 5~15중량부를 포함하고； 종단 방향으로 폭이 25~35cm으로 구성되고 20cm 이상의 간격으로 상하 관통된 관통공이 구성된 무채색의 중간부가 구성되고； 중간부를 제외한 부분이 검정색의 양측 가장자리부가 성되고； 블로운 필름 성형장치에서 110~130℃에서 압출되어； 저밀도 폴리에틸렌(LDPE) 등과 같은 합성수지를 전혀 사용하지 않아 토양 속에 매립되어 미생물의 대사 작용에 의해서 완전하게 생분해되고 환경호르몬 및 유독가스 배출이 없고 조성물의 용융온도가 낮아 공정 시간이 단축되고 무채색 중간부와 가장자리의 검정색으로 구성되어 고구마 재배용 적합하고 칼슘이 포함되어 토양 중에 방치하여도 산성 토양을 개선하고 식물이나 과일에 칼슘의 영양분을 공급하는 등의 효과가 있다.