PROBLEM TO BE SOLVED: To provide a dental curable composition highly suppressing polymerization shrinkage while giving high mechanical strength to a cured product.SOLUTION: A dental curable composition contains (A) an aromatic radical-polymerizable monomer, (B) an aliphatic radical-polymerizable monomer, (C) a dendritic polymer, suitably a hyperbranched polymer, (D) a filler and (E) a polymerization initiator, where the mass ratio of the (A) aromatic radical-polymerizable monomer and the (B) aliphatic radical-polymerizable monomer is 55/45 to 85/15 and where the compounding amount of the (C) dendritic polymer is 5 to 50 pts.mass and the compounding amount of the (D) filler is 150 to 1500 pts.mass, based on the total amount, 100 pts.mass, of the (A) aromatic radical-polymerizable monomer and the (B) aliphatic radical-polymerizable monomer.COPYRIGHT: (C)2014,JPO&INPIT【課題】 重合収縮率を高度に抑制しつつ、硬化体の高い機械的強度が得られる歯科用硬化性組成物を提供すること。【解決手段】 (A)芳香族系ラジカル重合性単量体、(B)脂肪族系ラジカル重合性単量体、(C)樹枝状ポリマー、好適にはハイパーブランチポリマー、(D)充填材、および(E)重合開始剤を含有してなる歯科用硬化性組成物であって、(A)芳香族系ラジカル重合性単量体および(B)脂肪族系ラジカル重合性単量体の質量比が55/45~85/15であり、(A)芳香族系ラジカル重合性単量体および(B)脂肪族系ラジカル重合性単量体の合計量100質量部に対して、(C)樹枝状ポリマーの配合量が5~50質量部であり、且つ(D)充填材の配合量が150~1500質量部であることを特徴とする歯科用硬化性組成物。【選択図】 なし