The present invention comprises the steps of (1) reacting a cellulose raw material with an alkalizing agent to obtain an alkalized cellulose； (2) reacting the alkalized cellulose with a carboxymethylating agent to obtain carboxymethyl cellulose； (3) a primary crosslinking step of reacting the carboxymethyl cellulose with a core crosslinking agent to obtain a crosslinked carboxymethyl cellulose in a slurry state； (4) filtering the crosslinked carboxymethyl cellulose in the slurry state, washing and dehydrating； (5) a secondary crosslinking step of reacting the crosslinked carboxymethyl cellulose obtained in step (4) with a foaming agent and a surface crosslinking agent to obtain a porous carboxymethyl cellulose having a core-shell structure； And (6) drying and pulverizing the porous carboxymethyl cellulose having a core-shell structure to obtain porous carboxymethyl cellulose particles having a core-shell structure, by the method It relates to the prepared carboxymethyl cellulose particles and an absorbent article comprising the same.본 발명은 (1) 셀룰로오스 원료를 알칼리화제와 반응시켜 알칼리화 셀룰로오스를 얻는 단계； (2) 상기 알칼리화 셀룰로오스를 카르복시메틸화제와 반응시켜 카르복시메틸 셀룰로오스(carboxymethyl cellulose)를 얻는 단계； (3) 상기 카르복시메틸 셀룰로오스를 코어 가교제와 반응시켜 슬러리 상태의 카르복시메틸 셀룰로오스 가교체를 얻는 1차 가교 단계； (4) 상기 슬러리 상태의 카르복시메틸 셀룰로오스 가교체를 여과한 후, 세정 및 탈수하는 단계； (5) 상기 (4)단계를 거친 카르복시메틸 셀룰로오스 가교체를 발포제 및 표면 가교제와 반응시켜 코어-쉘 구조를 갖는 다공성 카르복시메틸 셀룰로오스를 얻는 2차 가교 단계； 및 (6) 상기 코어-쉘 구조를 갖는 다공성 카르복시메틸 셀룰로오스를 건조 및 분쇄하여 코어-쉘 구조를 갖는 다공성 카르복시메틸 셀룰로오스 입자를 얻는 단계；를 포함하는 카르복시메틸 셀룰로오스 입자의 제조방법, 상기 방법에 의해 제조된 카르복시메틸 셀룰로오스 입자 및 이를 포함하는 흡수성 물품에 관한 것이다.