A controllably degradable multi-(amino acid) copolymer-organic calcium/phosphor salt filling type composite bone implant and a preparation method. The composite bone implant consists of a multi-(amino acid) copolymer and a medically acceptable organic calcium/phosphor salt component. The organic calcium/phosphor salt accounts for 20-90% of the total mass of the composite material the multi-(amino acid) copolymer is formed by polymerizing ε-aminocaproic acid and at least two other amino acids the ε-aminocaproic acid accounts for at least 50% of the total molar weight of the amino acid copolymer the other amino acids account for at least 0.5% of the total molar weight of the amino acid copolymer respectively. The composite bone implant is more suitable for the healing and repairing period of a human bodys natural bone, the pH value of a soaking liquid of the composite bone implant after degradation is 6.5-7.5, the partial physiological environment is slightly affected, irritative reaction is not caused, and the cell growth and the tissue repair are facilitated.Linvention concerne un implant osseux composite de type remplissage à base de copolymère multi(acides aminés)-sel organique de calcium/phosphore à dégradation contrôlée et un procédé de préparation.Limplant osseux composite est constitué dun copolymère de multi-(acides aminés) et dun composant sel organique de calcium/phosphore médicalement acceptable. Le sel organique de calcium/phosphore représente de 20 à 90 % de la masse totale du matériau composite le copolymère de multi(acides aminés) est formé par polymérisation dacide ε-aminocaproïque et dau moins deux autres acides aminés lacide ε-aminocaproïque représente au moins 50 % de la masse molaire totale du copolymère dacides aminés les autres acides aminés représentent au moins 0,5 % de la masse molaire totale du copolymère dacides aminés respectivement. Limplant osseux composite est plus approprié pour la période de cicatrisation et de réparation dun os na