The invention relates to a process for preparing microporous ceramic granules to be employed in the plastic bone surgery. According to the invention, the process consists in that, in a first stage, there is prepared a stable ceramic suspension of controlled rheology, in admixture with 0.5...2% surface-active/dispersing substances and it is homogenized with a polymeric solution of 1...4% sodium alginate of controlled viscosity, after which, in the second stage, the ceramic microspheres are formed using non-miscible liquids technique, by dropping the composite suspension into the gel-making solution, the so formed microspheres being then washed, dried and finally sintered at a temperature of 1100...1250°C, depending on their composition, wherefrom there are obtained granules suitable for use in the osteosynthesis process.Invenţia se referă la un procedeu pentru obţinerea unor granule ceramice microporoase, cu utilizare în chirurgia osoasă reparatorie. Procedeul conform invenţiei constă din aceea că, într-o primă etapă, se prepară o suspensie ceramică stabilă, cu reologie controlată cu adaos de 0,5...2% substanţe tensioactive/dispersante, şi omogenizarea acesteia cu o soluţie polimerică de 1...4% de alginat de sodiu, cu viscozitate controlată, după care, în etapa următoare, are loc formarea microsferelor ceramice prin tehnica lichidelor nemiscibile, prin picurarea suspensiei de compozit în soluţia de gelifiere, microsferele formate sunt spălate, uscate şi, în final, sinterizate la o temperatură de 1100...1250°C, în funcţie de compoziţie, rezultând granule adecvate pentru utilizare în procesul de osteosinteză.