The present invention relates to a cement composition and a method for producing a dental, more specifically C 3 S (Tricalcium silicate: 3CaO SiO 2 preparing a first composition consisting of particles ) -C 2 S (Dicalcium silicate: 2CaO SiO 2 ) preparing a second composition consisting of particles C 3 A (Tricalcium aluminate: 3CaO Al 2 O 3 ) as a third composition comprising particles of the preparation phase And each is weighed but a mixture prepared of the first composition, the second composition and third composition particles comprises the steps of preparing a cement composition for dentistry, comprising: preparing the first composition, the second composition or third composition particles : is the weighed at a predetermined mol C 3 S, -C 2 S, or C 3 a certain amount of isopropyl alcohol (isopropyl after mixing in the alcohol), stirring for a predetermined time using a ball mill (ball mill) It stirred the C 3 S, -C 2 S, or C 3 for a period in the mixture constant temperature of A and isopropyl alcohol hours drying Dry the C 3 S, -C 2 S, or heat-treating the C 3 A And heat treating said C 3 S, -C 2 S or C 3 A crushed to particles of a certain size, which includes the steps of and the features.본 발명은 치과용 시멘트 조성물 및 이의 제조방법에 관한 것으로, 보다 구체적으로는 C3S(Tricalcium silicate : 3CaO·SiO2)로 이루어진 제1조성물 입자를 준비하는 단계 β-C2S(Dicalcium silicate : 2CaO·SiO2)로 이루어진 제2조성물 입자를 준비하는 단계 C3A(Tricalcium aluminate : 3CaO·Al2O3)로 이루어진 제3조성물 입자를 준비하는 단계 및 각각 칭량되어 준비된 상기 제1조성물, 제2조성물 및 제3조성물 입자를 혼합하여 치과용 시멘트 조성물을 제조하는 단계를 포함하되, 상기 제1조성물, 제2조성물 또는 제3조성물 입자를 준비하는 단계:는 일정 mol로 칭량된 상기 C3S, β-C2S 또는 C3A를 일정량의 이소프로필알콜(isopropyl alcohol)에 혼합한 후, 볼 밀(ball mill)을 이용하여 일정시간 동안 교반하는 단계 교반된 상기 C3S, β-C2S 또는 C3A와 이소프로필알콜의 혼합물을 일정온도에서 일정시간 동안 건조하는 단계 건조된 상기 C3S, β-C2S 또는 C3A를 열처리하는 단계 및 열처리된 상기 C3S, β-C2S 또는 C3A를 일정크기의 입자로 분쇄하는 단계를 포함하는 것을 특징으로 한다.