A method for preparing a porous tantalum medical implant material comprises: mixing a pure tantalum powder with a binding agent to obtain tantalum powder slurry placing into a steel die a high polymer resin template support which has the porosity of 20% to 50% and is completely connected in a three-dimensional way pouring the prepared tantalum powder slurry into the steel die and submerging the high polymer resin template support in the steel die slowly and uniformly applying pressure at the periphery of the steel die so that the tantalum powder is completely and fully filled into the high polymer resin template support, the applied pressure being increased from 0 MPa to 8-12 MPa at a constant speed and the time required by the pressure application process being 2-5 h performing chemical dissolution to remove the high polymer resin template support to obtain a green body framework of porous tantalum and finally, performing posttreatment such as degreasing, sintering, and cooling to obtain a biomedical porous tantalum implant material. The prepared porous tantalum implant material has good biocompatibility and an excellent mechanical property.Un procédé de préparation dun matériau dimplant médical en tantale poreux comprend les étapes consistant à : mélanger une poudre de tantale pur et un liant afin dobtenir une bouillie de poudre de tantale placer dans un moule en acier un support de gabarit en une résine de haut polymère dont la porosité est comprise entre 20 et 50 % et qui est entièrement relié dune manière tridimensionnelle verser la bouillie de poudre de tantale préparée dans le moule en acier et immerger le support de gabarit en une résine de haut polymère dans le moule en acier appliquer lentement et uniformément une pression à la périphérie du moule en acier, de telle sorte que la poudre de tantale est entièrement et complètement déversée dans le support de gabarit en une résine de haut polymère, la pression appliquée passant de 0 Mpa à 8-12 Mpa à une vit