The present invention relates to a method for preparing a dental pulp restorative material which has a short curing time and high operatability, causes no harmful action upon dental pulp to provide high bio-affinity, and regenerates dentine effectively. The method according to the present invention comprises the steps of: i) homogeneously mixing calcium phosphate dibasic with calcium carbonate at a Ca/P molar ratio of 1.5 and 2.0 to provide -tri-calcium phosphate and tetra-calcium phosphate, respectively； ii) mixing powder including -tri-calcium phosphate, tetra-calcium phosphate and dicalcium phosphate dihydrate mixed at a weight ratio of 6:2:2 with zirconium oxide (ZrO_2) at a weight ratio of 7:3； and iii) adding a mixed solution containing an ammonium hydrogen phosphate solution and a citric acid solution to the mixture obtained from step ii).본 발명은 짧은 경화시간을 가지고, 조작성이 뛰어나고, 치수에 유해작용이 없어 우수한 생체친화성을 가지며, 효과적으로 상아질을 재생시킬 수 있도록 한 치수수복재의 제조방법에 관한 것으로, i) 제2인산칼슘(Calcium Phosphate Dibasic)과 탄산칼슘(Calcium Carbonate)을 각각 Ca/P몰비 1.5와 2.0으로 균일 혼합하여 α-트리-칼슘 포스페이트(α-Tri-Calcium Phosphate) 및 테트라-칼슘 포스페이트(Tetra-Calcium Phosphate)를 합성하는 제 1 단계, ii) α-트리-칼슘 포스페이트(α-Tri-Calcium Phosphate), 테트라-칼슘 포스페이트(Tetra-Calcium Phosphate), 디칼슘 포스페이트 디하이드레이트(Dicalcium phosphate Dihydrate)를 중량비 6:2:2로 혼합한 분말과 산화지르코늄(ZrO2)을 중량비 7:3의 비율로 혼합하는 제 2 단계 및 iii) 상기 제 2 단계에서 제조된 혼합물에 인산수소 암모늄(Ammonium Hydrogen Phosphate) 용액과 시트르산(Citric Acid) 용액을 혼합한 용액을 가하는 제 3 단계를 포함하여 이루어지는 것을 특징으로 한다.