The present invention relates to a zirconia surface treating agent for artificial teeth and a surface treating method. More specifically, in the present invention, provided are a zirconia surface treating agent for artificial teeth and a surface treating method using the same. In the present invention, the surface treating agent comprises 45wt% of sodium carbonate (Na^2Co^3)； 45wt% of potassium carbonate (K^2CO^3)； and 10wt% of aluminum oxide (Al^2O^3). The surface treating method comprises a sandblast treating step of treating the zirconia surface for artificial teeth in a sandblast with use of alumina powders whose size is 50 &mu；m.본 발명은 인공치아용 지르코니아 표면처리제 및 표면처리방법에 관한 것으로, 본 발명에 의한 표면처리제는 탄산나트륨(Sodium Carbonate, Na2co3) 45중량%, 탄산칼륨(Potassium Carbonate, K2CO3) 45중량%, 산화알루미늄(Aluminum Oxide, Al2O3) 10중량%의 조성으로 구성되며, 지르코니아의 표면처리방법은 50㎛크기의 알루미나(Alumina) 분말로 인공치아용 지르코니아의 표면을 샌드블라스트(Sandblast) 처리하는 샌드블라스팅 단계와, 상기 샌드블라스팅 단계를 거친 지르코니아를 탄산나트륨(Sodium Carbonate, Na2co3) 45중량%, 탄산칼륨(Potassium Carbonate, K2CO3) 45중량%, 산화알루미늄(Aluminum Oxide, Al2O3) 10중량%의 조성으로 구성되며 에틸알코올을 통해 혼합된 표면처리제에 매몰시키는 매몰단계와, 상기 매몰단계를 거친 지르코니아를 전기로에 넣고 5℃/min의 승온속도로 900℃∼1000℃로 가열하는 가열단계와, 상기 가열단계 후에 2시간을 유지한 후 상온으로 냉각시키는 냉각단계와, 상기 냉각단계를 거친 후에 알칼리 처리된 지르코니아를 50% 염산에 넣어 알칼리를 용출한 후 물로 세척하는 알칼리 용출 및 세척단계로 구성된다.따라서 지르코니아 소재로 된 인공치아의 표면을 처리하여 표면조도를 증가시킴으로써 레진 시멘트와의 접합강도를 증가시켜 지르코니아 인공치아 시술 후의 탈리 현상을 방지되는 효과가 있으며, 인공치아의 접합강도 증진으로 시술 후 박리에 의한 보수율을 감소시킴으로써 경제적, 시간적 손실을 감소시키는 효과가 있고, 지르코니아 소재로 된 인공치아에 대한 표면처리제의 개발로 표면처리제의 생산 및 판매에 필요한 새로운 일자리가 창출을 기대할 수 있는 매우 유용한 발명이다.