PROBLEM TO BE SOLVED: To provide a polyvinylidene fluoride-based resin fishline which is high in tensile strength and knot strength, has a fewer fish-eye defects, has excellent flexural abrasion characteristics, thus is more excellent in durability.SOLUTION: A monofilament is provided by melt-spinning a resin composition in which 0.001-10 pts.wt. diorganopolysiloxane compound is combined with 100 pts.wt. polyvinylidene fluoride resin. The tensile strength is 600-760 MPa, the knot strength is 475-550 MPa, the number of fish-eye defects extending parallel to the fiber axis is 6 or less per 20 mm of length, and the reciprocation of a friction element until the monofilament is broken is 5,000 times or more in a flexural abrasion test measured according to the regulation of JIS L-1095-7.10.2B.COPYRIGHT: (C)2012,JPO&INPIT【課題】引張強度および結節強度が高く、フィッシュアイ状欠陥数が少ないことにより、優れた屈曲摩耗特性を有することから、従来よりも耐久性に優れたポリフッ化ビニリデン系樹脂製釣糸を提供する。【解決手段】ポリフッ化ビニリデン樹脂100重量部に対し、ジオルガノポリシロキサン化合物0.001~10重量部を配合した樹脂組成物を溶融紡糸してなるモノフィラメントであって、その引張強度が600~760MPa、結節強度が475~550MPa、繊維軸に平行に伸びたフィッシュアイ状欠陥数が長さ20mm当たり6個以下かつ、JIS L-1095-7.10.2Bの規定に準じて測定した屈曲摩耗試験においてモノフィラメントが切断するまでの摩擦子の往復回数が5000回以上であることを特徴とする釣糸。【選択図】なし