ADHÉSIF À L'URÉE-FORMALDÉHYDE À FAIBLE ÉMISSION DE FORMALDÉHYDE, UTILE POUR LA FABRICATION DE PANNEAUX EN BOIS, COMPRENANT DES NANOFIBRES DE CELLULOSE ET DES NANOPARTICULES DE CUIVRE； PROCÉDÉ D'OBTENTION DE CELUI-CI
A low-formaldehyde-emitting urea-formaldehyde adhesive, with enhanced mechanical properties and high durability, useful for the manufacture of wooden boards, comprising: (a) urea (U) and formaldehyde (F), in F/U molar ratios of 0.9 to 1.2； (b) 1.3-1.7% w/w cellulose nanofibres (CNFs) with a width of between 46 and 60 nm； and (c) 0.4-0.6% w/w copper nanoparticles with a diameter of between 30 and 100 nm. The invention also relates to the method for producing the adhesive.Un adhesivo Urea-formaldehído de baja emisión de formaldehído, con propiedades mecánicas superiores y alta durabilidad, útil para la fabricación de tableros de madera, que comprende: (a) Urea (U) y Formaldehído (F) en razones molares F/U de 0,9 a 1,2； (b) 1,3 – 1,7 % p/p de nanofibrilas de celulosa (NFC) con un ancho entre 45 – 60 nm； y (c) 0,4 – 0,6 % p/p de nanopartículas de cobre con tamaño entre 30 a 100 nm. Además, de su proceso de elaboración.La présente invention concerne un adhésif à l'urée-formaldéhyde à faible émission de formaldéhyde présentant des propriétés mécaniques supérieures et une haute durabilité, utile pour la fabrication de panneaux en bois, qui comprend: (a) de l'urée (U) et du formaldéhyde (F) suivant des rapports molaires F/U de 0,9 à 1,2； (b) de 1,3 à 1,7 % p/p de nanofibrilles de cellulose (NFC) avec une largeur de 45 à 60 nm； et (c) de 0,4 à 0,6 % p/p de nanoparticules de cuivre avec une taille comprise entre 30 et 10 nm. L'invention concerne également le procédé d'élaboration dudit adhésif.