The invention relates to a method to increase the strength of a form body of lithium silicate glass ceramic, which after it has a desired end geometry and after the application of a material which influences its surface to form a coating, is subject to a heat treatment. To create a surface compressive stress through the replacement of lithium ions by alkali ions of greater diameter at least that region not covered by the application layer is covered by a melt or paste consisting of or containing a salt of an alkali metal with ions of greater diameter and the form body is in contact with the melt or paste for a period of time t at a temperature T and the melt or paste is subsequently removed from the form body.L'invention concerne un procédé pour augmenter la résistance d'un corps de forme en vitrocéramique à base de silicate de lithium, qui après avoir acquis une géométrie finale souhaitée et après l'application d'un matériau qui agit sur sa surface pour former un revêtement, est soumis à un traitement thermique. Afin de créer une contrainte de compression de surface par le remplacement des ions lithium par des ions alcalins de plus grand diamètre, au moins la région non recouverte par la couche d'application est recouverte par une matière fondue ou une pâte constituée de ou contenant un sel d'un métal alcalin avec des ions de diamètre plus grand et le corps de forme est en contact avec la matière fondue ou la pâte pendant une période de temps t à une température T et la matière fondue ou la pâte est ensuite retirée du corps de forme.