PROBLEM TO BE SOLVED: To provide an agricultural film having superior mechanical strength and heat-resistant fusion bonding properties.SOLUTION: A layer (A) including polyethylene-based resin having a density of 0.900 to 0.930 g/cmand a melt flow rate (MFR) of 0.3 to 5.0 g/10 min or ethylene-vinyl acetate copolymer having a vinyl acetate content of 5.0 to 25 wt.% and a MFR of 0.5 to 4.0 g/10 min, a layer (B) including ethylene-vinyl acetate copolymer having a vinyl acetate content of 5.0 to 25 wt.% and a MFR of 0.5 to 4.0 g/10 min, and a layer (C) including a polyethylene-based resin having a density of 0.900 to 0.930 g/cmand a MFR of 0.3 to 5.0 g/10 min are laminated and integrated in this order. At least one of the layer (A) or the layer (C) includes 0.1 to 0.5 pts.wt. silica particles having a particle size of 5 to 10 μm based on 100 pts.wt. resin components included in each layer.【課題】機械的強度及び耐熱融着性に優れた農業用フィルムを提供する。【解決手段】密度が０．９００～０．９３０ｇ／ｃｍ3で且つメルトフローレイト（ＭＦＲ）が０．３～５．０ｇ／１０分であるポリエチレン系樹脂、又は酢酸ビニル含有量が５．０～２５重量％で且つＭＦＲが０．５～４．０ｇ／１０分であるエチレン－酢酸ビニル共重合体を含む層（Ａ）、酢酸ビニル含有量が５．０～２５重量％で且つＭＦＲが０．５～４．０ｇ／１０分であるエチレン－酢酸ビニル共重合体を含む層（Ｂ）、及び密度が０．９００～０．９３０ｇ／ｃｍ3で且つＭＦＲが０．３～５．０ｇ／１０分であるポリエチレン系樹脂を含む層（Ｃ）が、この順で積層一体化されてなり、上記層（Ａ）又は上記層（Ｃ）のうちの少なくとも一方が、各層に含まれる樹脂成分１００重量部に対して、粒子径が５～１０μｍのシリカ粒子を０．１～０．５重量部含む農業用フィルム。【選択図】なし